PLASTISOL GLITTER ADHESIVE

High washing fastness is achieved when printing under the specified conditions.

•Curing: 1.5-2.5 minutes at 150-170°C
•Squeegee Rubber: 50-60A Shore
•Cleaning: Synthetic thinner
•Storage: 10-30°C
•Packaging: 10 kg, 30 kg and 60 kg plastic

WATER BASED GLITTER ADHESIVE

High washing fastness is achieved when printing under the specified conditions.

•Curing: 1.5-2.5 minutes at 150-160°C
•Cleaning: Water and sponge
•Storage: 5-30°C
•Packaging: 10 kg, 30 kg and 60 kg plastic

PLASTISOL FOIL ADHESIVE

High washing fastness is achieved when printing under the specified conditions.

•Fixation: 1.0-1.5 minutes at 150-160°C
•Foil Printing: 150-170°C, 4-6 bar, 15-20 seconds
•Silk No: 43T
•Squeegee Hardness: 50-60A Shore
•Cleaning: Synthetic thinner
•Storage: 10-30°C
•Packaging: 10 kg, 30 kg and 60 kg plastic

SOLVENT BASED FOIL ADHESIVE
SMOG

Solvent-based polyurethane adhesive for gravure printing technique.
High washing fastness is achieved when printing under the specified conditions.

Various recipes can be applied using TVS-075 (crosslinker/hardener), TVS-05 (catalyst/accelerator) and MEK.
The mixture (TVS-100, TVS-075&TVS-005) is applied on the back of the foil with a gravure cylinder.
Semi-dried at 60-80 °C.
The foil is printed on the textile surface by calendering at 120-150°C.
The reaction (curing) should be completed within 24-48 hours in a hot room at 50-80°C.
The carrier film of the foil is separated after curing is completed.
It is sold in 60 kg plastic packaging.

SOLVENT BASED FOIL ADHESIVE
SMOG

Solvent-based polyurethane adhesive for gravure printing technique.
High washing fastness is achieved when printing under the specified conditions.

Various recipes can be applied using TVS-070 (crosslinker/hardener), TVS-05 (catalyst/accelerator) and MEK.
The mixture (TVS-110, TVS-070&TVS-005) is applied on the back of the foil with a gravure cylinder.
Semi-dried at 60-80 °C.
The foil is printed on the textile surface by calendering at 120-150°C.
The reaction (curing) should be completed within 24-48 hours in a hot room at 50-80°C.
The carrier film of the foil is separated after curing is completed.
It is sold in 60 kg plastic packaging.

WATER BASED FOIL ADHESIVE

Water-based adhesive used in textile hot foil printing applications.
High washing fastness is achieved when printing under the specified conditions.
Washing tests should be performed 24 hours after foil printing.

• Fixation: 150-160°C for 1.5-2.5 minutes
• Foil Printing: 150-170°C, 4-6 bar, 15-20 seconds
• Mesh No: 43T
• Squeegee Blade: 50-60A Shore
• Cleaning: Water and sponge
• Storage: 5-30°C
• Packaging: 10 kg, 30 kg and 60 kg plastic

WATER BASED FOIL ADHESIVE
ECO

Water-based adhesive used in textile hot foil printing applications.
High washing fastness is achieved when printing under the specified conditions.
Washing tests should be performed 24 hours after foil printing.

• Fixation: 150-160°C for 1.5-2.5 minutes
• Foil Printing: 150-170°C, 4-6 bar, 15-20 seconds
• Mesh No: 43T
• Squeegee Blade: 50-60A Shore
• Cleaning: Water and sponge
• Storage: 5-30°C
• Packaging: 10 kg, 30 kg and 60 kg plastic

WATER BASED FLEXCOAT ADHESIVE
SPRAYING

TVW-FX is a water-based adhesive used in leather hot press applications.
Specially developed in a flexible structure suitable for the elastic structure of the Flexcoat foil.
Allows the ground and foil to stretch together.
After the product is dried with fixation, flexcoat printing should be done in rotopress at 140-160°C and 15-20 bar pressure, and in leather press at 110-115°C and 100 bar pressure.
High rubbing fastness is achieved when printing is done under the specified conditions.
Should be stored with its lid closed between 5-30°C.
Should not be exposed to direct sunlight.
It is in 10 kg, 20 kg, 30 kg and 60 kg plastic packages.

WATER BASED FOIL ADHESIVE
SPRAYING

Water-based adhesive used in textile hot printing applications.
High washing fastness is achieved when printing under the specified conditions.
It should be shaken before use.
Washing tests should be done 24 hours after foil printing.

•Fixation: 150-160°C for 1.5-2.5 minutes
•Foil Printing: 150-170°C, 4-6 bar, 15-20 seconds
•Squeegee Hardness: 50-60A Shore
•Cleaning: Water and sponge
•Storage: 5-30°C
•Packaging: 10 kg, 20 kg, 30 kg and 60 kg plastic

WATER BASED FOIL ADHESIVE
ECO
SPRAYING

Water-based adhesive used in textile hot printing applications.
High washing fastness is achieved when printing under the specified conditions.
It should be shaken before use.
Washing tests should be done 24 hours after foil printing.

•Fixation: 150-160°C for 1.5-2.5 minutes
•Foil Printing: 150-170°C, 4-6 bar, 15-20 seconds
•Squeegee Hardness: 50-60A Shore
•Cleaning: Water and sponge
•Storage: 5-30°C
•Packaging: 10 kg, 20 kg, 30 kg and 60 kg plastic

WATER BASED FOIL ADHESIVE
SUPER
SPRAYING

Water-based adhesive used in textile hot printing applications.
High washing fastness is achieved when printing under the specified conditions.
It should be shaken before use.
Washing tests should be done 24 hours after foil printing.

•Fixation: 150-160°C for 1.5-2.5 minutes
•Foil Printing: 150-170°C, 4-6 bar, 15-20 seconds
•Squeegee Hardness: 50-60A Shore
•Cleaning: Water and sponge
•Storage: 5-30°C
•Packaging: 10 kg, 20 kg, 30 kg and 60 kg plastic